Título: CARACTERIZAÇÃO DE PAINÉIS COMPENSADOS DE Pinus sp. ANÁLISE DAS PROPRIEDADES FÍSICAS E MEC NICAS COM ADESIVO POLIURETANO

Autoria de: Victor Guimarães Arantes

Orientação de: Lourival Marin Mendes

Coorientação de: Douglas Lamounier Faria

Presidente da banca: Lourival Marin Mendes

Primeiro membro da banca: Jose Benedito Guimaraes Junior

Segundo membro da banca: Douglas Lamounier Faria

Terceiro membro da banca: Laércio Mesquita Júnior

Palavras-chaves: Caracterização de painéis, gramaturas, epifluorescência, qualidade da linha de cola, adesivo alternativo

Data da defesa: 24/11/2023

Semestre letivo da defesa: 2023-2

Data da versão final: 08/12/2023

Data da publicação: 08/12/2023

Referência: Arantes, V. G. CARACTERIZAÇÃO DE PAINÉIS COMPENSADOS DE Pinus sp. ANÁLISE DAS PROPRIEDADES FÍSICAS E MEC NICAS COM ADESIVO POLIURETANO. 2023. 41 p. Trabalho de Conclusão de Curso (Graduação em Engenharia Florestal Bacharelado)-Universidade Federal de Lavras, Lavras, 2023.

Resumo: No contexto industrial da produção de painéis compensados de madeira, a escolha do adesivo adequado desempenha um papel determinante na garantia da qualidade e durabilidade dos painéis. Nesse sentido, este trabalho teve como objetivo avaliar as propriedades físicas e mecânicas de painéis compensados produzidos com madeira de Pinus sp. e adesivo poliuretano em diferentes gramaturas. Ao contrário dos adesivos fenólicos tradicionais, o poliuretano tem se destacado devido às suas propriedades superiores de adesão, resistência à umidade e maior durabilidade, além de não emitir formaldeído. Foram produzidos painéis compensados compostos por cinco lâminas de 2 mm de espessura, utilizando diferentes gramaturas de adesivo poliuretano (240, 280 e 320 gm²). Os painéis foram submetidos a testes físicos, incluindo avaliação de umidade, densidade aparente e absorção de água, e a testes mecânicos, como flexão estática nas posições flatwise e edgewise e resistência ao cisalhamento, além de análise de epifluorescência da lin

Abstract: In the industrial context of wood veneer plywood production, the selection of the appropriate adhesive plays a crucial role in ensuring the quality and durability of the panels. In this regard, this study aimed to assess the physical and mechanical properties of plywood panels manufactured with Pinus sp. wood and polyurethane adhesive at different weight per unit areas. Unlike traditional phenolic adhesives, polyurethane has stood out due to its superior properties of adhesion, moisture resistance, increased durability, and the absence of formaldehyde emission. Plywood panels composed of five layers with a thickness of 2 mm each were produced, using varying weights of polyurethane adhesive (240, 280, and 320 gm²). The panels underwent physical tests, including moisture evaluation, apparent density, and water absorption, as well as mechanical tests such as static bending in flatwise and edgewise positions, shear strength, and analysis of adhesive line epifluorescence. The observed results revealed that the re

URI: sip.prg.ufla.br/publico/trabalhos_conclusao_curso/acessar_tcc_por_curso/
engenharia_florestal/20232201810507

URI alternaviva: sem URI do Repositório Institucional da UFLA até o momento.

Curso: G005 - ENGENHARIA FLORESTAL (BACHARELADO)

Nome da editora: Universidade Federal de Lavras

Sigla da editora: UFLA

País da editora: Brasil

Gênero textual: Trabalho de Conclusão de Curso

Nome da língua do conteúdo: Português

Código da língua do conteúdo: por

Licença de acesso: Acesso aberto

Nome da licença: Licença do Repositório Institucional da Universidade Federal de Lavras

URI da licença: repositorio.ufla.br

Termos da licença: Acesso aos termos da licença em repositorio.ufla.br

Detentores dos direitos autorais: Victor Guimarães Arantes e Universidade Federal de Lavras

Baixar arquivo